| STYLE# |
9417 |
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| DESCRIPTION / CONSTRUCTION |
| |
|
|
|
|
|
|
|
|
|
|
|
|
| DOUBLE COATED CBR PROTECTIVE |
|
|
|
|
|
|
|
|
|
|
|
|
| AREAS OF APPLICATIONS |
| |
|
|
|
|
|
|
|
|
|
|
|
|
| SUBMITTED FOR TOXICOLOGICAL TESTING |
|
|
|
|
|
|
|
|
|
|
|
|
| CHARACTERITICS / PHYSICAL PROPERTIES |
| |
|
|
|
|
|
|
|
|
|
|
|
|
| TEST / METHOD |
|
|
|
Federal Standard 191A or ASTM |
|
|
REQUIREMENT |
|
|
|
|
|
|
|
|
|
|
|
|
|
| COLOR FINISH |
|
|
|
VISUAL |
|
|
TAN |
|
| WEIGHT (Oz/Yd² MIN
TO MAX) |
|
ASTM D 751 |
|
6.8 TO 8.0 |
| BREAKING STRENGTH (LBS
MIN) "Grab Method" |
ASTM D 751 |
|
Warp: 50 Fill:
45 |
| BREAKING STRENGTH AFTER
WEATHERING (LBS MIN) "Grab Method" |
ASTM D 751 "WEATHEROMETER REQUIRED ONLY ON PREPRODUCTION SAMPLES." |
Warp: 40 Fill:
35 |
| PUNCTURE RESISTANCE (LBS MIN) |
|
PARA. 4.4.3.10 |
|
10 |
| COATING ADHESION (LBS./2 INCHES WIDTH, MIN) |
|
FED. STD. 191A METHOD
5970 |
4.0 |
| HYDROSTATIC RESISTANCE (PSI MIN) |
|
PARA.4.4.3.9 & ASTM
D 751 |
60 |
| ABRASION RESISTANCE (VISUAL
PASS OR FAIL) |
|
FED. STD. 191A METHOD
5302 |
NO BASE FABRIC SHALL BE EXPOSED. |
| RUBBER PROPERTIES: TENSILE
STRENGTH, MIN |
|
ASTM D 412 |
|
1800.0 |
| RUBBER PROPERTIES: ELONGATION,
MIN |
|
ASTM D 412 |
|
350 |
| RUBBER PROPERTIES: 300%
MODULUS, MIN |
|
ASTM D 412 |
|
1200 |
| RUBBER PROPERTIES: SPECIFIC
GRAVTY, MIN TO MAX |
|
|
1.21 TO 1.27 |
|
|
|
|
|
|
|
| The
information contained herein was developed in our laboratories and is
believed reliable. It is offered in good faith. However, |
|
| as prospective users conditions
and methods of use are beyond our control, we recommend the user determine
the suitability |
|
| of this product before adapting
our materials on a commercial scale. |
|
|
|
|
|
|
|
|
|
|
|
|
|