Engineered Coated Fabrics |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
| STYLE# |
9232 |
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| DESCRIPTION / CONSTRUCTION |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Butyl Coated Cloth, Toxicological
Agents Protective |
|
|
|
|
|
|
|
|
|
|
|
|
|
| AREAS OF APPLICATIONS |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Mil-C-12189 (SAND COLOR) |
|
|
|
|
|
|
|
|
|
|
|
|
|
| CHARACTERITICS / PHYSICAL PROPERTIES |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
| TEST / METHOD |
|
|
|
Federal Standard 191A or ASTM |
|
|
REQUIREMENT |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| COLOR FINISH |
|
|
|
VISUAL |
|
|
SAND |
|
| WIDTH (INCHES
TRIMMED) |
|
|
|
|
60" |
|
|
|
| WEIGHT (gm/m² MIN
TO MAX) |
|
METHOD ASTM
D 751 |
|
350 to 425 |
|
| BREAKING STRENGTH (Kg/50 mm MIN) |
|
METHOD ASTM
D 751 |
|
Warp: 70 Fill:
60 |
|
|
|
| B/S AFTER WEATHERING 100 HOURS % LOSS |
|
METHOD ASTM
D 751 |
|
Warp: 90% Fill:
90% |
|
|
|
| CLARK STIFFNESS AT
70° F CMS |
|
METHOD
5204-1 FED-STD-191A |
|
Warp: 9.5 |
|
|
|
| CLARK STIFFNESS AT
-20° F CMS |
|
METHOD
5204-1 FED-STD-191A |
|
Warp: 11.0 |
|
|
|
| CLARK STIFFNESS AFTER WEATHERING 100 HOURS % LOSS (WARP & FILL,
MIN) |
|
METHOD
5204-1 FED-STD-191A |
|
10% Over Initial |
|
|
| ADHESION (Kg./50mm., MIN) |
|
METHOD ASTM
D 751 |
|
3.0 |
|
|
|
| TEAR STRENGTH gm.
Minimum |
|
METHOD ASTM
D 1424 |
|
Warp: 1200 Fill:
1000 |
|
|
|
| HYDROSTATIC RESITANCE
Kg/cm² minimum |
|
METHOD
5512 FED-STD-191A |
|
12.0 |
|
|
|
| HYDROSTATIC RESITANCE
AFTER COLD CRACK AT -40° F Kg/cm² min. |
METHOD 5874 & 5512 FED-STD-191A |
|
12.0 |
|
|
|
| The
information contained herein was developed in our laboratories and is
believed reliable. It is offered in good faith. However, |
|
| as prospective users conditions
and methods of use are beyond our control, we recommend the user determine
the suitability |
|
| of this product before adapting
our materials on a commercial scale. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|